PMNT Substrate (011) 10x10x0.5mm, two sides polished - PMNTg101005S2
Substrate Specifications
- Size: 10x10x 0.5mm +/-0.05mm
-
Orientation: (011 ) +/-0.5 Deg
-
Growing Method: Bridgman method
- Polish: two sides EPI polished by CMP technology with less sub-surface lattice damage.
- Surface finish(Ra): < 10 A
- Pack: Packed in 100 grade plastic bag under 1000 class clean room.
- Warning: PMNT crystal has a visible twin on a polished surface, which is normal nature .
Typical Properies
|
ChemicalComposition: |
( PbMg 0.33 Nb 0.67)1-x: (PbTiO3)x; x=0.29-0.32 |
|
Crystalstructure / Lattice |
|
|
Melting Point: |
1280 oC |
|
Density |
8.1 g/cm3 |
|
Piezoelectric Coefficient |
d33 m >2000 pC/N |
|
Coupling Constant |
|
|
Dielectric Constant |
e (at 1kHz after poling) 4000 |
|
Dielectric loss |
tan delta < 0.9 |
|
Curie temperature: |
135-150 oC |
|
Max size |
25 mm x 25 mm x 1- 2 mm thickness along [001], |
Related Products
|
LaAlO3 |
MgO |
YSZ |
SrLaAlO4 |
|
|
|
|
|
|
Dicing Saw |
RTP Furnace |
Wafer Containers |
Film Coaters |
|
|
|
|
 |
Original: $425.00
-65%$425.00
$148.75PMNT Substrate (011) 10x10x0.5mm, two sides polished - PMNTg101005S2
Substrate Specifications
- Size: 10x10x 0.5mm +/-0.05mm
-
Orientation: (011 ) +/-0.5 Deg
-
Growing Method: Bridgman method
- Polish: two sides EPI polished by CMP technology with less sub-surface lattice damage.
- Surface finish(Ra): < 10 A
- Pack: Packed in 100 grade plastic bag under 1000 class clean room.
- Warning: PMNT crystal has a visible twin on a polished surface, which is normal nature .
Typical Properies
|
ChemicalComposition: |
( PbMg 0.33 Nb 0.67)1-x: (PbTiO3)x; x=0.29-0.32 |
|
Crystalstructure / Lattice |
|
|
Melting Point: |
1280 oC |
|
Density |
8.1 g/cm3 |
|
Piezoelectric Coefficient |
d33 m >2000 pC/N |
|
Coupling Constant |
|
|
Dielectric Constant |
e (at 1kHz after poling) 4000 |
|
Dielectric loss |
tan delta < 0.9 |
|
Curie temperature: |
135-150 oC |
|
Max size |
25 mm x 25 mm x 1- 2 mm thickness along [001], |
Related Products
|
LaAlO3 |
MgO |
YSZ |
SrLaAlO4 |
|
|
|
|
|
|
Dicing Saw |
RTP Furnace |
Wafer Containers |
Film Coaters |
|
|
|
|
|
Product Information
Product Information
Shipping & Returns
Shipping & Returns
Description
Substrate Specifications
- Size: 10x10x 0.5mm +/-0.05mm
-
Orientation: (011 ) +/-0.5 Deg
-
Growing Method: Bridgman method
- Polish: two sides EPI polished by CMP technology with less sub-surface lattice damage.
- Surface finish(Ra): < 10 A
- Pack: Packed in 100 grade plastic bag under 1000 class clean room.
- Warning: PMNT crystal has a visible twin on a polished surface, which is normal nature .
Typical Properies
|
ChemicalComposition: |
( PbMg 0.33 Nb 0.67)1-x: (PbTiO3)x; x=0.29-0.32 |
|
Crystalstructure / Lattice |
|
|
Melting Point: |
1280 oC |
|
Density |
8.1 g/cm3 |
|
Piezoelectric Coefficient |
d33 m >2000 pC/N |
|
Coupling Constant |
|
|
Dielectric Constant |
e (at 1kHz after poling) 4000 |
|
Dielectric loss |
tan delta < 0.9 |
|
Curie temperature: |
135-150 oC |
|
Max size |
25 mm x 25 mm x 1- 2 mm thickness along [001], |
Related Products
|
LaAlO3 |
MgO |
YSZ |
SrLaAlO4 |
|
|
|
|
|
|
Dicing Saw |
RTP Furnace |
Wafer Containers |
Film Coaters |
|
|
|
|
|