LSAT (100) 10x10 x0.5 mm square substrate, 2 sides polished - LSATa101005S2
HomeStore

LSAT (100) 10x10 x0.5 mm square substrate, 2 sides polished - LSATa101005S2

LSAT (100) 10x10 x0.5 mm square substrate, 2 sides polished - LSATa101005S2

LSAT (LaAlO3)0.3 (Sr2AlTaO6)0.7   is a newly developing crystal  with peroviskite structure and twin-free.  LSAT has excellent lattice match with high Tc superconductors and many oxide materials. LSAT has lower melting point and  can be grown by CZ technology at lower cost, therefore, it is expected to replace LaAlO3 and SrTiO3 as a common single crystal substrate for epitaxial oxide thin films for gain magnetic ferro-electronic and superconductive devices

Click here to view SDS
 
Substrate Specifications:
Size:  10 x 10 x 0.5 mm +/-0.05 mm
Orientation:     <100> +/-0.5 Deg
Surface Roughness:   CMP polished two sides with min. sub-surface damage , and Ra < 10 A
Package:   Packing in 1000 class clean room  with 100 grade clean plastic bag

 

 

Typical Physical Properties

Chemical Formula

( LaAlO3)0.3 (Sr2AlTaO6)0.7    or  ( La0.18Sr0.82)(Al0.59Ta0.41)O3

Crystal Structure

cubic:             a = 3.868 A

Growth Method

Czochralski

Density

6.74   g/cm3

Melt Point

1840  oC        

Thermal expansion

 10 (x10-6/ oC)

Dielectric Constant

~ 22

Color and Appearance

Colorless to light brown based on annealing condition.   No twin and domain visible


Customers Who Bought This Item Also Bought

 LSAT

LaAlO3

 MgO

 NdCaAlO4

NdGaO3

 SrTiO3

SrLaAlO4

 SrLaGaO4

YSZ

 

$135.00
LSAT (100) 10x10 x0.5 mm square substrate, 2 sides polished - LSATa101005S2—
$135.00

LSAT (100) 10x10 x0.5 mm square substrate, 2 sides polished - LSATa101005S2

LSAT (LaAlO3)0.3 (Sr2AlTaO6)0.7   is a newly developing crystal  with peroviskite structure and twin-free.  LSAT has excellent lattice match with high Tc superconductors and many oxide materials. LSAT has lower melting point and  can be grown by CZ technology at lower cost, therefore, it is expected to replace LaAlO3 and SrTiO3 as a common single crystal substrate for epitaxial oxide thin films for gain magnetic ferro-electronic and superconductive devices

Click here to view SDS
 
Substrate Specifications:
Size:  10 x 10 x 0.5 mm +/-0.05 mm
Orientation:     <100> +/-0.5 Deg
Surface Roughness:   CMP polished two sides with min. sub-surface damage , and Ra < 10 A
Package:   Packing in 1000 class clean room  with 100 grade clean plastic bag

 

 

Typical Physical Properties

Chemical Formula

( LaAlO3)0.3 (Sr2AlTaO6)0.7    or  ( La0.18Sr0.82)(Al0.59Ta0.41)O3

Crystal Structure

cubic:             a = 3.868 A

Growth Method

Czochralski

Density

6.74   g/cm3

Melt Point

1840  oC        

Thermal expansion

 10 (x10-6/ oC)

Dielectric Constant

~ 22

Color and Appearance

Colorless to light brown based on annealing condition.   No twin and domain visible


Customers Who Bought This Item Also Bought

 LSAT

LaAlO3

 MgO

 NdCaAlO4

NdGaO3

 SrTiO3

SrLaAlO4

 SrLaGaO4

YSZ

 

Product Information

Shipping & Returns

Description

LSAT (LaAlO3)0.3 (Sr2AlTaO6)0.7   is a newly developing crystal  with peroviskite structure and twin-free.  LSAT has excellent lattice match with high Tc superconductors and many oxide materials. LSAT has lower melting point and  can be grown by CZ technology at lower cost, therefore, it is expected to replace LaAlO3 and SrTiO3 as a common single crystal substrate for epitaxial oxide thin films for gain magnetic ferro-electronic and superconductive devices

Click here to view SDS
 
Substrate Specifications:
Size:  10 x 10 x 0.5 mm +/-0.05 mm
Orientation:     <100> +/-0.5 Deg
Surface Roughness:   CMP polished two sides with min. sub-surface damage , and Ra < 10 A
Package:   Packing in 1000 class clean room  with 100 grade clean plastic bag

 

 

Typical Physical Properties

Chemical Formula

( LaAlO3)0.3 (Sr2AlTaO6)0.7    or  ( La0.18Sr0.82)(Al0.59Ta0.41)O3

Crystal Structure

cubic:             a = 3.868 A

Growth Method

Czochralski

Density

6.74   g/cm3

Melt Point

1840  oC        

Thermal expansion

 10 (x10-6/ oC)

Dielectric Constant

~ 22

Color and Appearance

Colorless to light brown based on annealing condition.   No twin and domain visible


Customers Who Bought This Item Also Bought

 LSAT

LaAlO3

 MgO

 NdCaAlO4

NdGaO3

 SrTiO3

SrLaAlO4

 SrLaGaO4

YSZ

 

LSAT (100) 10x10 x0.5 mm square substrate, 2 sides polished - LSATa101005S2 | MTI Online Store