1700 Grade Sintered Zirconia ( Cao stabilized Ceramic Board, 150 mm x 150 mm x 5.0 mm (1 pc) - (1 pc)-CZB1505
1700 Grade Sintered Zirconia ( Cao stabilized Ceramic Board, 150 mm x 150 mm x 5.0 mm (1 pc) - (1 pc)-CZB1505
EQ-CZB-150-5 is a calcium stabilized zirconia ceramic board as a base liner for sintering high purity ceramic parts without contamination. It is used for MTI high-temperature box ( muffle ) furnace.
Size: 150 mm x 150 mm x 5 mm thickness
Specifications
Size: 150 mm x 150 mm x 5 mm thickness
Specifications
Parameter |
Data |
Al2O3 |
≤0.5% |
SiO2 |
≤0.5% |
Fe2O3 |
≤0.09% |
ZrO+CaO |
≥98.5% |
Density |
4.3-4.6 g/cm3 |
Porous rate |
22-26 % |
Compressive strength |
20 Mpa |
Thermal expension @1100 |
0.8-0.9% |
Max.working temperature |
1700 |
$99.00
1700 Grade Sintered Zirconia ( Cao stabilized Ceramic Board, 150 mm x 150 mm x 5.0 mm (1 pc) - (1 pc)-CZB1505—
$99.00
1700 Grade Sintered Zirconia ( Cao stabilized Ceramic Board, 150 mm x 150 mm x 5.0 mm (1 pc) - (1 pc)-CZB1505
EQ-CZB-150-5 is a calcium stabilized zirconia ceramic board as a base liner for sintering high purity ceramic parts without contamination. It is used for MTI high-temperature box ( muffle ) furnace.
Size: 150 mm x 150 mm x 5 mm thickness
Specifications
Size: 150 mm x 150 mm x 5 mm thickness
Specifications
Parameter |
Data |
Al2O3 |
≤0.5% |
SiO2 |
≤0.5% |
Fe2O3 |
≤0.09% |
ZrO+CaO |
≥98.5% |
Density |
4.3-4.6 g/cm3 |
Porous rate |
22-26 % |
Compressive strength |
20 Mpa |
Thermal expension @1100 |
0.8-0.9% |
Max.working temperature |
1700 |
Product Information
Product Information
Shipping & Returns
Shipping & Returns
Description
EQ-CZB-150-5 is a calcium stabilized zirconia ceramic board as a base liner for sintering high purity ceramic parts without contamination. It is used for MTI high-temperature box ( muffle ) furnace.
Size: 150 mm x 150 mm x 5 mm thickness
Specifications
Size: 150 mm x 150 mm x 5 mm thickness
Specifications
Parameter |
Data |
Al2O3 |
≤0.5% |
SiO2 |
≤0.5% |
Fe2O3 |
≤0.09% |
ZrO+CaO |
≥98.5% |
Density |
4.3-4.6 g/cm3 |
Porous rate |
22-26 % |
Compressive strength |
20 Mpa |
Thermal expension @1100 |
0.8-0.9% |
Max.working temperature |
1700 |