Single-Side Coated S/C Disk (D15 mm) as Cathode of Li-S Battery for CR20XX Coin Cells, 50 pcs/pack - bcaf-SCCss-D15
HomeStore

Single-Side Coated S/C Disk (D15 mm) as Cathode of Li-S Battery for CR20XX Coin Cells, 50 pcs/pack - bcaf-SCCss-D15

Single-Side Coated S/C Disk (D15 mm) as Cathode of Li-S Battery for CR20XX Coin Cells, 50 pcs/pack - bcaf-SCCss-D15

This electrode sheet is based on Aluminum foil coated by S/C composite. Sulfur-Carbon Composite (S/C) with high conductivity and uniform mixing features can be used as high performance cathode for Li-S battery testing

SPECIFICATIONS

  • Material: S/C Composite 
  • Current collector (substrate): Aluminum foil (15-16 microns, area density of 4.22mg/cm2)
  • Single sides area density: 4.1 ± 0.1 mg/cm2
  • Compaction density: 2.8 ± 0.1 g/cm3
  • Coating Thickness: ~38 um
  • Total Thickness: ~54 um
  • Active Material Proportion in Powder: 94% 
  • Specific Capacity: ~1260 mAh/g (0.25C), ~1100 mAh/g (0.5C). [DOL:DME =1:1, 1 mol/L LiTFSI, testing voltage range: 1.5-2.6 V]    
   
  • Note:  The electrode sheet shall be stored in a vacuum box, a vacuum oven or a glove box to avoid degradation.                     
$86.80

Original: $248.00

-65%
Single-Side Coated S/C Disk (D15 mm) as Cathode of Li-S Battery for CR20XX Coin Cells, 50 pcs/pack - bcaf-SCCss-D15—

$248.00

$86.80

Single-Side Coated S/C Disk (D15 mm) as Cathode of Li-S Battery for CR20XX Coin Cells, 50 pcs/pack - bcaf-SCCss-D15

This electrode sheet is based on Aluminum foil coated by S/C composite. Sulfur-Carbon Composite (S/C) with high conductivity and uniform mixing features can be used as high performance cathode for Li-S battery testing

SPECIFICATIONS

  • Material: S/C Composite 
  • Current collector (substrate): Aluminum foil (15-16 microns, area density of 4.22mg/cm2)
  • Single sides area density: 4.1 ± 0.1 mg/cm2
  • Compaction density: 2.8 ± 0.1 g/cm3
  • Coating Thickness: ~38 um
  • Total Thickness: ~54 um
  • Active Material Proportion in Powder: 94% 
  • Specific Capacity: ~1260 mAh/g (0.25C), ~1100 mAh/g (0.5C). [DOL:DME =1:1, 1 mol/L LiTFSI, testing voltage range: 1.5-2.6 V]    
   
  • Note:  The electrode sheet shall be stored in a vacuum box, a vacuum oven or a glove box to avoid degradation.                     

Product Information

Shipping & Returns

Description

This electrode sheet is based on Aluminum foil coated by S/C composite. Sulfur-Carbon Composite (S/C) with high conductivity and uniform mixing features can be used as high performance cathode for Li-S battery testing

SPECIFICATIONS

  • Material: S/C Composite 
  • Current collector (substrate): Aluminum foil (15-16 microns, area density of 4.22mg/cm2)
  • Single sides area density: 4.1 ± 0.1 mg/cm2
  • Compaction density: 2.8 ± 0.1 g/cm3
  • Coating Thickness: ~38 um
  • Total Thickness: ~54 um
  • Active Material Proportion in Powder: 94% 
  • Specific Capacity: ~1260 mAh/g (0.25C), ~1100 mAh/g (0.5C). [DOL:DME =1:1, 1 mol/L LiTFSI, testing voltage range: 1.5-2.6 V]    
   
  • Note:  The electrode sheet shall be stored in a vacuum box, a vacuum oven or a glove box to avoid degradation.                     