PE Battery Separator Roll by Wet Method (500m-1500 m L × 60 mm W × 20 um T) - Lib-PE6020
PE Battery Separator Roll by Wet Method (1500 m L × 60 mm W × 20 um T) can be used as an excellent Li ion battery separator.
Specifications
- Material: Polyethylene (PE)
- Thickness: 20 ± 2 um
- Width : 60 mm
-
Air Permeability: 230±60 s/100ml
- Porosity: 44 ± 5 %
- Area Density: 10.6.2±3.0 g/m2
- Puncture Strength : ≥600 G
- Tensile Strength: ≥ 1600 Kgf/cm2 (MD); ≥ 1400 Kgf/cm2 (TD)
- Thermal Shrinkage: ≤2.5% (MD); ≤1.0% (TD). Drying at 90℃ for 2 h.
-
Sold in roll only
-
Select Length
From $58.80
Original: $168.00
-65%PE Battery Separator Roll by Wet Method (500m-1500 m L × 60 mm W × 20 um T) - Lib-PE6020—
$168.00
$58.80PE Battery Separator Roll by Wet Method (500m-1500 m L × 60 mm W × 20 um T) - Lib-PE6020
PE Battery Separator Roll by Wet Method (1500 m L × 60 mm W × 20 um T) can be used as an excellent Li ion battery separator.
Specifications
- Material: Polyethylene (PE)
- Thickness: 20 ± 2 um
- Width : 60 mm
-
Air Permeability: 230±60 s/100ml
- Porosity: 44 ± 5 %
- Area Density: 10.6.2±3.0 g/m2
- Puncture Strength : ≥600 G
- Tensile Strength: ≥ 1600 Kgf/cm2 (MD); ≥ 1400 Kgf/cm2 (TD)
- Thermal Shrinkage: ≤2.5% (MD); ≤1.0% (TD). Drying at 90℃ for 2 h.
-
Sold in roll only
-
Product Information
Product Information
Shipping & Returns
Shipping & Returns
Description
PE Battery Separator Roll by Wet Method (1500 m L × 60 mm W × 20 um T) can be used as an excellent Li ion battery separator.
Specifications
- Material: Polyethylene (PE)
- Thickness: 20 ± 2 um
- Width : 60 mm
-
Air Permeability: 230±60 s/100ml
- Porosity: 44 ± 5 %
- Area Density: 10.6.2±3.0 g/m2
- Puncture Strength : ≥600 G
- Tensile Strength: ≥ 1600 Kgf/cm2 (MD); ≥ 1400 Kgf/cm2 (TD)
- Thermal Shrinkage: ≤2.5% (MD); ≤1.0% (TD). Drying at 90℃ for 2 h.
-
Sold in roll only
-