Nickel Felt Roll (1000mm L x 200 mm W x 0.45 mm T) as Conductive Substrate for Flow Battery, Fuel Cells, and Electrolyzer - EQ-bcnf-045m
Nickel Felt Roll (1000mm L x 200 mm W x 0.45 mm T) as Conductive Substrate for Flow Battery, Fuel Cells, and Electrolyzer - EQ-bcnf-045m
Specifications
-
Material: Nickel Felt Roll, Purity> 99.99% (excellent anti-corrosive)
-
Dimension/Property:
-
Length: 1000 mm
-
Width: 200mm
-
Thickness: 0.45 mm
- Porosity: 82%
-
- Notice: Please notice that it is normal to observe NiO peaks in the nickel foam in XRD data. It is really difficult to avoid the oxidation of the nickel.
- How to clean the Nickel Foam for Battery Cathode Substrate.
- It can be removed from the NiO by annealing in the hydrogen furnace.
-
Nickel fel sheet can be carefully cleaned with the concentrated HCl solution (37 wt.%) in an ultrasound bath for 5 min in order to remove the surface oxide layer. And then deionized water and absolute ethanol were used for 5 min each to ensure the surface of the Ni foam was well cleaned.
More Images
Nickel Felt Roll (1000mm L x 200 mm W x 0.45 mm T) as Conductive Substrate for Flow Battery, Fuel Cells, and Electrolyzer - EQ-bcnf-045m
Specifications
-
Material: Nickel Felt Roll, Purity> 99.99% (excellent anti-corrosive)
-
Dimension/Property:
-
Length: 1000 mm
-
Width: 200mm
-
Thickness: 0.45 mm
- Porosity: 82%
-
- Notice: Please notice that it is normal to observe NiO peaks in the nickel foam in XRD data. It is really difficult to avoid the oxidation of the nickel.
- How to clean the Nickel Foam for Battery Cathode Substrate.
- It can be removed from the NiO by annealing in the hydrogen furnace.
-
Nickel fel sheet can be carefully cleaned with the concentrated HCl solution (37 wt.%) in an ultrasound bath for 5 min in order to remove the surface oxide layer. And then deionized water and absolute ethanol were used for 5 min each to ensure the surface of the Ni foam was well cleaned.
Product Information
Product Information
Shipping & Returns
Shipping & Returns
Description
Specifications
-
Material: Nickel Felt Roll, Purity> 99.99% (excellent anti-corrosive)
-
Dimension/Property:
-
Length: 1000 mm
-
Width: 200mm
-
Thickness: 0.45 mm
- Porosity: 82%
-
- Notice: Please notice that it is normal to observe NiO peaks in the nickel foam in XRD data. It is really difficult to avoid the oxidation of the nickel.
- How to clean the Nickel Foam for Battery Cathode Substrate.
- It can be removed from the NiO by annealing in the hydrogen furnace.
-
Nickel fel sheet can be carefully cleaned with the concentrated HCl solution (37 wt.%) in an ultrasound bath for 5 min in order to remove the surface oxide layer. And then deionized water and absolute ethanol were used for 5 min each to ensure the surface of the Ni foam was well cleaned.