LiNiCoAlO2 (Ni:Co:Al=8.15:1.5:0.35) Powder for High Power Li-ion Battery Cathode 200g/bottle - Lib-LNCA810
LiNiCoAlO2 (Ni:Co:Al=8.15:1.5:0.35) Powder for High Power Li-ion Battery Cathode 200g/bottle - Lib-LNCA810
LiNiCoAlO2 (Lithium Nickel Cobalt Aluminum Oxide) powder for Li-ion power battery cathode 200g/bottle (Ni:Co:Al =8.15:1.5:0.35)
Specification
| Item | Description | |
| Composition |
Li (NiCoAl) O2 Ni:Co:Al=8.15:1.5:0.35 |
Li = (7.2Ā Ā± 0.4)% Ni+Co+Al = (59.0Ā Ā± 1.0)% |
| D10 (Ī¼m) | 7.3 | |
| D50 (Ī¼m) | 13.6 | |
| D90Ā (Ī¼m) | 26.8 | |
| DmaxĀ (Ī¼m) | 39.9 | |
| Moisture | 380 | |
| pH | 11.7 | |
| Li2CO3 (%) | 0.32 | |
| LiOH (%) | 0.11 | |
| Fe (ppm) | ā¤100 ppm | |
| Na (ppm) | ā¤200 ppm | |
| Cu (ppm) | ā¤20 ppm | |
| Specific Surface Area (m2/g) | 0.5 | BET Analyzer |
| Tapped Density (g/cm3) | 2.40 | |
| Discharge Capacity (3.0-4.3V) (mAh/g) | 195.7 | @ 0.1C |
| Discharge Rate (%) | 90.0 | @2C vs.0.2C |
| Capacity Retention (RT, 3.0-4.3V, 1C/1C) (%) | 92.3 | Ā 1C@51cls |
| Optional | You may order precursor to may your own composition ( click below link to order:
NiCoAl Precursor Powder (Ni0.8Co0.15Al0.05OH2 ) for DIY High Capacity Li-Ion Battery Cathode Powder 200g/bottle - EQ-Lib-Pre-NCA |
|
Application Notes:
- Please click to see Procedure forĀ Preparing Anode & Cathode Electrode Slurry.
- Please keep the powder in vacuum box to avoid moisture.
- Please bake the powder in a vacuum oven at 120 - 150 Ā°C before making slurry and coating to ensure max. capacity.
- This product is not manufactured by MTI. We onlyĀ sell small quantity to help the researcher developing new battery. If you have any question onĀ IP conflict, let us know. We will forward the question toĀ the manufacturer.Ā
Related Products
 Vacuum Storage Box |
 Powder Milling & Mixer |
Ā  Electrode Coaters |
 Battery Research Equipment |
 Other Battery Powders |
 Solid Electrolyte |
Ā
Ā
$298.00
LiNiCoAlO2 (Ni:Co:Al=8.15:1.5:0.35) Powder for High Power Li-ion Battery Cathode 200g/bottle - Lib-LNCA810ā
$298.00
LiNiCoAlO2 (Ni:Co:Al=8.15:1.5:0.35) Powder for High Power Li-ion Battery Cathode 200g/bottle - Lib-LNCA810
LiNiCoAlO2 (Lithium Nickel Cobalt Aluminum Oxide) powder for Li-ion power battery cathode 200g/bottle (Ni:Co:Al =8.15:1.5:0.35)
Specification
| Item | Description | |
| Composition |
Li (NiCoAl) O2 Ni:Co:Al=8.15:1.5:0.35 |
Li = (7.2Ā Ā± 0.4)% Ni+Co+Al = (59.0Ā Ā± 1.0)% |
| D10 (Ī¼m) | 7.3 | |
| D50 (Ī¼m) | 13.6 | |
| D90Ā (Ī¼m) | 26.8 | |
| DmaxĀ (Ī¼m) | 39.9 | |
| Moisture | 380 | |
| pH | 11.7 | |
| Li2CO3 (%) | 0.32 | |
| LiOH (%) | 0.11 | |
| Fe (ppm) | ā¤100 ppm | |
| Na (ppm) | ā¤200 ppm | |
| Cu (ppm) | ā¤20 ppm | |
| Specific Surface Area (m2/g) | 0.5 | BET Analyzer |
| Tapped Density (g/cm3) | 2.40 | |
| Discharge Capacity (3.0-4.3V) (mAh/g) | 195.7 | @ 0.1C |
| Discharge Rate (%) | 90.0 | @2C vs.0.2C |
| Capacity Retention (RT, 3.0-4.3V, 1C/1C) (%) | 92.3 | Ā 1C@51cls |
| Optional | You may order precursor to may your own composition ( click below link to order:
NiCoAl Precursor Powder (Ni0.8Co0.15Al0.05OH2 ) for DIY High Capacity Li-Ion Battery Cathode Powder 200g/bottle - EQ-Lib-Pre-NCA |
|
Application Notes:
- Please click to see Procedure forĀ Preparing Anode & Cathode Electrode Slurry.
- Please keep the powder in vacuum box to avoid moisture.
- Please bake the powder in a vacuum oven at 120 - 150 Ā°C before making slurry and coating to ensure max. capacity.
- This product is not manufactured by MTI. We onlyĀ sell small quantity to help the researcher developing new battery. If you have any question onĀ IP conflict, let us know. We will forward the question toĀ the manufacturer.Ā
Related Products
|
Vacuum Storage Box |
Powder Milling & Mixer |
Ā Electrode Coaters |
Battery Research Equipment |
Other Battery Powders |
Solid Electrolyte |
Ā
Ā
Product Information
Product Information
Shipping & Returns
Shipping & Returns
Description
LiNiCoAlO2 (Lithium Nickel Cobalt Aluminum Oxide) powder for Li-ion power battery cathode 200g/bottle (Ni:Co:Al =8.15:1.5:0.35)
Specification
| Item | Description | |
| Composition |
Li (NiCoAl) O2 Ni:Co:Al=8.15:1.5:0.35 |
Li = (7.2Ā Ā± 0.4)% Ni+Co+Al = (59.0Ā Ā± 1.0)% |
| D10 (Ī¼m) | 7.3 | |
| D50 (Ī¼m) | 13.6 | |
| D90Ā (Ī¼m) | 26.8 | |
| DmaxĀ (Ī¼m) | 39.9 | |
| Moisture | 380 | |
| pH | 11.7 | |
| Li2CO3 (%) | 0.32 | |
| LiOH (%) | 0.11 | |
| Fe (ppm) | ā¤100 ppm | |
| Na (ppm) | ā¤200 ppm | |
| Cu (ppm) | ā¤20 ppm | |
| Specific Surface Area (m2/g) | 0.5 | BET Analyzer |
| Tapped Density (g/cm3) | 2.40 | |
| Discharge Capacity (3.0-4.3V) (mAh/g) | 195.7 | @ 0.1C |
| Discharge Rate (%) | 90.0 | @2C vs.0.2C |
| Capacity Retention (RT, 3.0-4.3V, 1C/1C) (%) | 92.3 | Ā 1C@51cls |
| Optional | You may order precursor to may your own composition ( click below link to order:
NiCoAl Precursor Powder (Ni0.8Co0.15Al0.05OH2 ) for DIY High Capacity Li-Ion Battery Cathode Powder 200g/bottle - EQ-Lib-Pre-NCA |
|
Application Notes:
- Please click to see Procedure forĀ Preparing Anode & Cathode Electrode Slurry.
- Please keep the powder in vacuum box to avoid moisture.
- Please bake the powder in a vacuum oven at 120 - 150 Ā°C before making slurry and coating to ensure max. capacity.
- This product is not manufactured by MTI. We onlyĀ sell small quantity to help the researcher developing new battery. If you have any question onĀ IP conflict, let us know. We will forward the question toĀ the manufacturer.Ā
Related Products
|
Vacuum Storage Box |
Powder Milling & Mixer |
Ā Electrode Coaters |
Battery Research Equipment |
Other Battery Powders |
Solid Electrolyte |
Ā
Ā