Conductive Graphite Powder KS6 for Li-ion Battery Anode & Cathode, 170 g/bottle - Lib-CGP-KS6

Fixed Carbon (%)

• ≥99.89

Applications:

• For preparing Li-ion battery electrode material:
• Cathode: Cathode Powder + Conductive + PVDF + NMP
• Anode: Anode Powder + Conductive Graphite + PVDF + NMP (or SBR + CMC)
• Corrosion resistance to Potassium Hydroxide
• For anti-corrosion and high-temperature lubricant
• For preparing carbon resister, conducting dry film and electrolyte.
• Applied in the rubber and plastic as bulking agent.
• Applied in raw material of alloy.
• Applied in the chemical industry as catalyst.

Notes:

• Please click to see Procedure for Preparing Anode & Cathode Electrode Slurry.
• Please keep the powder in vacuum box to avoid moisture.
• Please bake the powder in a vacuum oven at 120-150 °C before making slury and coating to ensure Max. capacity.

Particle Size

D10: 1.5µm; D50: 3.4µm; D90: 6.2µm

Moisture Content (%)

• <0.1

Ash Content (%)

• <0.01

Al

• 6 ppm

Ca

• 32 ppm

Cu

• < 1 ppm

Cr

• 1 ppm

Co

• 1 ppm

Ni

• 2 ppm

Mo

• < 0.5 ppm

Si

• 94 ppm

Sb

• < 2 ppm

As

• < 0.5 ppm

Pb

• < 0.8 ppm

Ti

• 4 ppm

Fe

• 91 ppm

V

• 10 ppm

S

• 14 ppm

Crystal Size Lc(002)

• >60 nm

Interlayer Spacing c/2 (002)

• 0.3354 – 0.336 nm

Density (Xylene)

• 2.254 g/cm3

Specific Surface Area

• 21.7 m^2/g