Li-Ion Battery Cathode - Aluminum Foil Single Side Coated by LiNiCoMnO2 (Ni:Co:Mn=8:1:1, NCM811) (241mm L x 200mm W x 0.06mm T) 5 sheets/bag -bcaf-ncm811ss
Li-Ion Battery Cathode - Aluminum Foil Single Side Coated by LiNiCoMnO2 (Ni:Co:Mn=8:1:1, NCM811) (241mm L x 200mm W x 0.06mm T) 5 sheets/bag -bcaf-ncm811ss
This electrode sheet is based on Aluminum foil coated by Lithium Nickel Manganese Cobalt Oxide (NCM811) on a single side and can be used as the cathode of Li-Ion battery -- 5 sheets /bag
SPECIFICATIONS
- Material: LiNiCoMnO2 (8:1:1)
- Current collector (substrate): Aluminum foil (16 microns, area density of 4.22mg/cm2)
- Coated Area: 241mm L x 175mm W. The edge width of blank area is 12.5 mm for each side.
- Single sides area density: 10.5 ± 0.20 mg/cm2
- Compaction density: 2.75 ± 0.1 g/cm3
- Coating Thickness: ~38 um
- Total Thickness: ~54 um
- Active Material Weight: 4.21 g
- Active Material in Electrode Sheet: 95% (PVDF and Super P is 2% and 3%, respectively)
- Specific Capacity: 190 mAh/g [0.1C, 3.0-4.3 V vs Li/Li+, Half Cell] [Electrolyte:1.0M LiPF6 in EC:DMC:EMC=1:1:1 Vol% with 1.0%VC]
-
Note: The electrode sheet shall be stored in a vacuum box, a vacuum oven or a glove box to avoid degradation.
for NCM-
for Aluminum e
Li-Ion Battery Cathode - Aluminum Foil Single Side Coated by LiNiCoMnO2 (Ni:Co:Mn=8:1:1, NCM811) (241mm L x 200mm W x 0.06mm T) 5 sheets/bag -bcaf-ncm811ss
This electrode sheet is based on Aluminum foil coated by Lithium Nickel Manganese Cobalt Oxide (NCM811) on a single side and can be used as the cathode of Li-Ion battery -- 5 sheets /bag
SPECIFICATIONS
- Material: LiNiCoMnO2 (8:1:1)
- Current collector (substrate): Aluminum foil (16 microns, area density of 4.22mg/cm2)
- Coated Area: 241mm L x 175mm W. The edge width of blank area is 12.5 mm for each side.
- Single sides area density: 10.5 ± 0.20 mg/cm2
- Compaction density: 2.75 ± 0.1 g/cm3
- Coating Thickness: ~38 um
- Total Thickness: ~54 um
- Active Material Weight: 4.21 g
- Active Material in Electrode Sheet: 95% (PVDF and Super P is 2% and 3%, respectively)
- Specific Capacity: 190 mAh/g [0.1C, 3.0-4.3 V vs Li/Li+, Half Cell] [Electrolyte:1.0M LiPF6 in EC:DMC:EMC=1:1:1 Vol% with 1.0%VC]
-
Note: The electrode sheet shall be stored in a vacuum box, a vacuum oven or a glove box to avoid degradation.
- for NCM
-
for Aluminum e
Product Information
Product Information
Shipping & Returns
Shipping & Returns
Description
This electrode sheet is based on Aluminum foil coated by Lithium Nickel Manganese Cobalt Oxide (NCM811) on a single side and can be used as the cathode of Li-Ion battery -- 5 sheets /bag
SPECIFICATIONS
- Material: LiNiCoMnO2 (8:1:1)
- Current collector (substrate): Aluminum foil (16 microns, area density of 4.22mg/cm2)
- Coated Area: 241mm L x 175mm W. The edge width of blank area is 12.5 mm for each side.
- Single sides area density: 10.5 ± 0.20 mg/cm2
- Compaction density: 2.75 ± 0.1 g/cm3
- Coating Thickness: ~38 um
- Total Thickness: ~54 um
- Active Material Weight: 4.21 g
- Active Material in Electrode Sheet: 95% (PVDF and Super P is 2% and 3%, respectively)
- Specific Capacity: 190 mAh/g [0.1C, 3.0-4.3 V vs Li/Li+, Half Cell] [Electrolyte:1.0M LiPF6 in EC:DMC:EMC=1:1:1 Vol% with 1.0%VC]
-
Note: The electrode sheet shall be stored in a vacuum box, a vacuum oven or a glove box to avoid degradation.