Li-Ion Battery Cathode - Aluminum Foil Double Side Coated by Single-Crystalline LiNiCoMnO2 (Ni:Co:Mn=8:1:1, NCM811-SC) (241mm L x 200mm W x 0.06mm T), 5 sheets/bag -bcaf-ncm811ds-sc
Li-Ion Battery Cathode - Aluminum Foil Double Side Coated by Single-Crystalline LiNiCoMnO2 (Ni:Co:Mn=8:1:1, NCM811-SC) (241mm L x 200mm W x 0.06mm T), 5 sheets/bag -bcaf-ncm811ds-sc
This electrode sheet is based on Aluminum foil coated by Single-Crystalline Lithium Nickel Manganese Cobalt Oxide (NCM811-SC) on double side and can be used as the cathode of Li-Ion battery - 5 sheets /bag.
SPECIFICATIONS
- Material: Single Crystalline NCM811 (Lib-LNCM811-SCLN)
- Current collector (substrate): Aluminum foil (16 microns, area density of 4.22mg/cm2)
- Coated Area: 241mm L x 175mm W. The edge width of blank area is 12.5 mm for each side.
- Double sides area density: 21 ± 0.2 mg/cm2
- Compaction density: 3.3 g/cm3
- Active Material Weight: 4.21 g
- Active Material Proportion in Powder: 95% (PVDF and Super P is 2% and 3%, respectively)
- Specific Capacity: 190-200 mAh/g
-
Note: The electrode sheet shall be stored in a vacuum box, a vacuum oven or a glove box to avoid degradation.
for NCM-
for Aluminum
Original: $298.00
-65%$298.00
$104.30Li-Ion Battery Cathode - Aluminum Foil Double Side Coated by Single-Crystalline LiNiCoMnO2 (Ni:Co:Mn=8:1:1, NCM811-SC) (241mm L x 200mm W x 0.06mm T), 5 sheets/bag -bcaf-ncm811ds-sc
This electrode sheet is based on Aluminum foil coated by Single-Crystalline Lithium Nickel Manganese Cobalt Oxide (NCM811-SC) on double side and can be used as the cathode of Li-Ion battery - 5 sheets /bag.
SPECIFICATIONS
- Material: Single Crystalline NCM811 (Lib-LNCM811-SCLN)
- Current collector (substrate): Aluminum foil (16 microns, area density of 4.22mg/cm2)
- Coated Area: 241mm L x 175mm W. The edge width of blank area is 12.5 mm for each side.
- Double sides area density: 21 ± 0.2 mg/cm2
- Compaction density: 3.3 g/cm3
- Active Material Weight: 4.21 g
- Active Material Proportion in Powder: 95% (PVDF and Super P is 2% and 3%, respectively)
- Specific Capacity: 190-200 mAh/g
-
Note: The electrode sheet shall be stored in a vacuum box, a vacuum oven or a glove box to avoid degradation.
- for NCM
-
for Aluminum
Product Information
Product Information
Shipping & Returns
Shipping & Returns
Description
This electrode sheet is based on Aluminum foil coated by Single-Crystalline Lithium Nickel Manganese Cobalt Oxide (NCM811-SC) on double side and can be used as the cathode of Li-Ion battery - 5 sheets /bag.
SPECIFICATIONS
- Material: Single Crystalline NCM811 (Lib-LNCM811-SCLN)
- Current collector (substrate): Aluminum foil (16 microns, area density of 4.22mg/cm2)
- Coated Area: 241mm L x 175mm W. The edge width of blank area is 12.5 mm for each side.
- Double sides area density: 21 ± 0.2 mg/cm2
- Compaction density: 3.3 g/cm3
- Active Material Weight: 4.21 g
- Active Material Proportion in Powder: 95% (PVDF and Super P is 2% and 3%, respectively)
- Specific Capacity: 190-200 mAh/g
-
Note: The electrode sheet shall be stored in a vacuum box, a vacuum oven or a glove box to avoid degradation.
- for NCM
-
for Aluminum