Li-Ion Battery Cathode - Aluminum Foil Double Side Coated by LiNiCoMnO2 (Ni:Co:Mn=8:1:1, NCM811) (241mm L x 200mm W x 0.1mm T) 5 sheets/bag - bcaf-ncm811ds
Li-Ion Battery Cathode - Aluminum Foil Double Side Coated by LiNiCoMnO2 (Ni:Co:Mn=8:1:1, NCM811) (241mm L x 200mm W x 0.1mm T) 5 sheets/bag - bcaf-ncm811ds
This electrode sheet is based on Aluminum foil coated by Lithium Nickel Manganese Cobalt Oxide (NCM811) on double sides and can be used as the cathode of Li-Ion battery -- 5 sheets /bag
SPECIFICATIONS
- Material: LiNiCoMnO2 8:1:1)
- Current collector (substrate): Aluminum foil (16 microns, area desnityof 4.22mg/cm2)
- Coated Area: 241mm L x 175mm W. The edge width of blank area is 12.5 mm for each side.
- Double sides area density: 21 ± 0.4 mg/cm2
- Compaction density: 3.3 ± 0.1 g/cm3
- Coating Thickness: ~64 um
- Total Thickness: ~80 um
- Active Material Weight: 8.41 g
- Active Material Proportion in Powder: 95% (PVDF and Super P is 2% and 3%, respectively)
- Specific Capacity: 190 mAh/g
-
Note: The electrode sheet shall be stored in a vacuum box, a vacuum oven or a glove box to avoid degradation.
for NCM- for Aluminum
Li-Ion Battery Cathode - Aluminum Foil Double Side Coated by LiNiCoMnO2 (Ni:Co:Mn=8:1:1, NCM811) (241mm L x 200mm W x 0.1mm T) 5 sheets/bag - bcaf-ncm811ds
This electrode sheet is based on Aluminum foil coated by Lithium Nickel Manganese Cobalt Oxide (NCM811) on double sides and can be used as the cathode of Li-Ion battery -- 5 sheets /bag
SPECIFICATIONS
- Material: LiNiCoMnO2 8:1:1)
- Current collector (substrate): Aluminum foil (16 microns, area desnityof 4.22mg/cm2)
- Coated Area: 241mm L x 175mm W. The edge width of blank area is 12.5 mm for each side.
- Double sides area density: 21 ± 0.4 mg/cm2
- Compaction density: 3.3 ± 0.1 g/cm3
- Coating Thickness: ~64 um
- Total Thickness: ~80 um
- Active Material Weight: 8.41 g
- Active Material Proportion in Powder: 95% (PVDF and Super P is 2% and 3%, respectively)
- Specific Capacity: 190 mAh/g
-
Note: The electrode sheet shall be stored in a vacuum box, a vacuum oven or a glove box to avoid degradation.
- for NCM
- for Aluminum
Product Information
Product Information
Shipping & Returns
Shipping & Returns
Description
This electrode sheet is based on Aluminum foil coated by Lithium Nickel Manganese Cobalt Oxide (NCM811) on double sides and can be used as the cathode of Li-Ion battery -- 5 sheets /bag
SPECIFICATIONS
- Material: LiNiCoMnO2 8:1:1)
- Current collector (substrate): Aluminum foil (16 microns, area desnityof 4.22mg/cm2)
- Coated Area: 241mm L x 175mm W. The edge width of blank area is 12.5 mm for each side.
- Double sides area density: 21 ± 0.4 mg/cm2
- Compaction density: 3.3 ± 0.1 g/cm3
- Coating Thickness: ~64 um
- Total Thickness: ~80 um
- Active Material Weight: 8.41 g
- Active Material Proportion in Powder: 95% (PVDF and Super P is 2% and 3%, respectively)
- Specific Capacity: 190 mAh/g
-
Note: The electrode sheet shall be stored in a vacuum box, a vacuum oven or a glove box to avoid degradation.
- for NCM
- for Aluminum