Hot Melt Adhesive (Polymer Tape) for Heat Sealing Pouch Cell Tabs (200m L x 8mm W x 0.1mm Thickness) PLIB-HMA8L200
HomeStore

Hot Melt Adhesive (Polymer Tape) for Heat Sealing Pouch Cell Tabs (200m L x 8mm W x 0.1mm Thickness) PLIB-HMA8L200

Hot Melt Adhesive (Polymer Tape) for Heat Sealing Pouch Cell Tabs (200m L x 8mm W x 0.1mm Thickness) PLIB-HMA8L200

This hot melt adhesive/sealant is a must-have item specifically made for sealing tabs (Nickel or Aluminum) in between aluminum-made lamination film (pouch cell case).
*MTI sells tabs (4mm, 5mm, 8mm and 30mm) with this sealant and Aluminum lamination film for immediately use, please kindly order from here.
Specifications 

Color

  • Black

Thickness

  • 100 um

Width

  • 8mm

Length

  • 200m for 1 roll

Material

  • Enhanced Sulfurized Polymer Resin Material (3 Layers Lamination)

Outside Layers (Both Sides) Thermal Softening Index

  • 116ÂșC/ 3 Seconds/ 0.3Mpa/ 180ÂșC (Reference only)

Outside Layers (Both Sides) Thermal Melting Index

  • 135ÂșC/ 3 Seconds/ 0.3Mpa/ 180ÂșC (Reference only)

Middle Layers (Both Sides) Thermal Softening Index

  • 145ÂșC/ 3 Seconds/ 0.3Mpa/ 180ÂșC (Reference only)

Middle Layers (Both Sides) Thermal Melting Index

  • 175ÂșC/ 3 Seconds/ 0.3Mpa/ 180ÂșC (Reference only)

Removal Strength from Tab

  • > 15N/15mm

Removal Strength from Al Lamination Film (Cell Case)

  • > 35N/15mm

Resistance to LiPF6 Solution (1:1:1)

  • No Change in the Solution @ 85ÂșC*24 Hours
Packing
  • Sealed in vacuumed Al bag when shipping
Manual & Video
 Click the video below to see how to use MTI's heat sealer MSK-140 to seal the tab onto pouch cell cases by this adhesive (in video, we call it polymer tape):

 

 

 

 

 

$598.00
Hot Melt Adhesive (Polymer Tape) for Heat Sealing Pouch Cell Tabs (200m L x 8mm W x 0.1mm Thickness) PLIB-HMA8L200—
$598.00

Hot Melt Adhesive (Polymer Tape) for Heat Sealing Pouch Cell Tabs (200m L x 8mm W x 0.1mm Thickness) PLIB-HMA8L200

This hot melt adhesive/sealant is a must-have item specifically made for sealing tabs (Nickel or Aluminum) in between aluminum-made lamination film (pouch cell case).
*MTI sells tabs (4mm, 5mm, 8mm and 30mm) with this sealant and Aluminum lamination film for immediately use, please kindly order from here.
Specifications 

Color

  • Black

Thickness

  • 100 um

Width

  • 8mm

Length

  • 200m for 1 roll

Material

  • Enhanced Sulfurized Polymer Resin Material (3 Layers Lamination)

Outside Layers (Both Sides) Thermal Softening Index

  • 116ÂșC/ 3 Seconds/ 0.3Mpa/ 180ÂșC (Reference only)

Outside Layers (Both Sides) Thermal Melting Index

  • 135ÂșC/ 3 Seconds/ 0.3Mpa/ 180ÂșC (Reference only)

Middle Layers (Both Sides) Thermal Softening Index

  • 145ÂșC/ 3 Seconds/ 0.3Mpa/ 180ÂșC (Reference only)

Middle Layers (Both Sides) Thermal Melting Index

  • 175ÂșC/ 3 Seconds/ 0.3Mpa/ 180ÂșC (Reference only)

Removal Strength from Tab

  • > 15N/15mm

Removal Strength from Al Lamination Film (Cell Case)

  • > 35N/15mm

Resistance to LiPF6 Solution (1:1:1)

  • No Change in the Solution @ 85ÂșC*24 Hours
Packing
  • Sealed in vacuumed Al bag when shipping
Manual & Video
 Click the video below to see how to use MTI's heat sealer MSK-140 to seal the tab onto pouch cell cases by this adhesive (in video, we call it polymer tape):

 

 

 

 

 

Product Information

Shipping & Returns

Description

This hot melt adhesive/sealant is a must-have item specifically made for sealing tabs (Nickel or Aluminum) in between aluminum-made lamination film (pouch cell case).
*MTI sells tabs (4mm, 5mm, 8mm and 30mm) with this sealant and Aluminum lamination film for immediately use, please kindly order from here.
Specifications 

Color

  • Black

Thickness

  • 100 um

Width

  • 8mm

Length

  • 200m for 1 roll

Material

  • Enhanced Sulfurized Polymer Resin Material (3 Layers Lamination)

Outside Layers (Both Sides) Thermal Softening Index

  • 116ÂșC/ 3 Seconds/ 0.3Mpa/ 180ÂșC (Reference only)

Outside Layers (Both Sides) Thermal Melting Index

  • 135ÂșC/ 3 Seconds/ 0.3Mpa/ 180ÂșC (Reference only)

Middle Layers (Both Sides) Thermal Softening Index

  • 145ÂșC/ 3 Seconds/ 0.3Mpa/ 180ÂșC (Reference only)

Middle Layers (Both Sides) Thermal Melting Index

  • 175ÂșC/ 3 Seconds/ 0.3Mpa/ 180ÂșC (Reference only)

Removal Strength from Tab

  • > 15N/15mm

Removal Strength from Al Lamination Film (Cell Case)

  • > 35N/15mm

Resistance to LiPF6 Solution (1:1:1)

  • No Change in the Solution @ 85ÂșC*24 Hours
Packing
  • Sealed in vacuumed Al bag when shipping
Manual & Video
 Click the video below to see how to use MTI's heat sealer MSK-140 to seal the tab onto pouch cell cases by this adhesive (in video, we call it polymer tape):

 

 

 

 

 

Hot Melt Adhesive (Polymer Tape) for Heat Sealing Pouch Cell Tabs (200m L x 8mm W x 0.1mm Thickness) PLIB-HMA8L200 | MTI Online Store