Double Side LiFePO4 (LFP) Coated Aluminum Foil for Battery Cathode (20 m L x 200mm W x 90 um T), 1 Roll, - CAl-R-LFP
HomeStore

Double Side LiFePO4 (LFP) Coated Aluminum Foil for Battery Cathode (20 m L x 200mm W x 90 um T), 1 Roll, - CAl-R-LFP

Double Side LiFePO4 (LFP) Coated Aluminum Foil for Battery Cathode (20 m L x 200mm W x 90 um T), 1 Roll, - CAl-R-LFP

The graphite-coated copper foil in a roll can be used as anode for pouch cell testing.Ā 

SPECIFICATIONS

Graphite coating
  • Coating Thickness: ~117.4 um (double side coated)Ā 
  • Total Thickness: 133.4 um
    Foil Thickness: 16 um
  • Width: 200mm (coating width of 175 mm, left and right-hand side is 12.5 mm without coating), Length: 20 m/roll
  • Double sides material density: 27.0Ā±0.4 mg/cm2
  • Compaction density: 2.3 g/cm3
  • Active Material Proportion in Powder: 95.4% (PVDF and Super P is 2% and 2.6%, respectively)
Specific Capacity

150 mAh/g (Area Capacity: 3.864 mAh/cm2); 0.1 C; 2.5-3.7 V; Electrolyte: 1.0M LiPF6 in EC:DMC:EMC=1:1:1 Vol% with 1.0%VC

  • Charging and Discharging Curve for the First Cycle
  • Rate Testing
  • Cycling Test


$1,490.00
Double Side LiFePO4 (LFP) Coated Aluminum Foil for Battery Cathode (20 m L x 200mm W x 90 um T), 1 Roll, - CAl-R-LFPā€”
$1,490.00

Double Side LiFePO4 (LFP) Coated Aluminum Foil for Battery Cathode (20 m L x 200mm W x 90 um T), 1 Roll, - CAl-R-LFP

The graphite-coated copper foil in a roll can be used as anode for pouch cell testing.Ā 

SPECIFICATIONS

Graphite coating
  • Coating Thickness: ~117.4 um (double side coated)Ā 
  • Total Thickness: 133.4 um
    Foil Thickness: 16 um
  • Width: 200mm (coating width of 175 mm, left and right-hand side is 12.5 mm without coating), Length: 20 m/roll
  • Double sides material density: 27.0Ā±0.4 mg/cm2
  • Compaction density: 2.3 g/cm3
  • Active Material Proportion in Powder: 95.4% (PVDF and Super P is 2% and 2.6%, respectively)
Specific Capacity

150 mAh/g (Area Capacity: 3.864 mAh/cm2); 0.1 C; 2.5-3.7 V; Electrolyte: 1.0M LiPF6 in EC:DMC:EMC=1:1:1 Vol% with 1.0%VC

  • Charging and Discharging Curve for the First Cycle
  • Rate Testing
  • Cycling Test


Product Information

Shipping & Returns

Description

The graphite-coated copper foil in a roll can be used as anode for pouch cell testing.Ā 

SPECIFICATIONS

Graphite coating
  • Coating Thickness: ~117.4 um (double side coated)Ā 
  • Total Thickness: 133.4 um
    Foil Thickness: 16 um
  • Width: 200mm (coating width of 175 mm, left and right-hand side is 12.5 mm without coating), Length: 20 m/roll
  • Double sides material density: 27.0Ā±0.4 mg/cm2
  • Compaction density: 2.3 g/cm3
  • Active Material Proportion in Powder: 95.4% (PVDF and Super P is 2% and 2.6%, respectively)
Specific Capacity

150 mAh/g (Area Capacity: 3.864 mAh/cm2); 0.1 C; 2.5-3.7 V; Electrolyte: 1.0M LiPF6 in EC:DMC:EMC=1:1:1 Vol% with 1.0%VC

  • Charging and Discharging Curve for the First Cycle
  • Rate Testing
  • Cycling Test


Double Side LiFePO4 (LFP) Coated Aluminum Foil for Battery Cathode (20 m L x 200mm W x 90 um T), 1 Roll, - CAl-R-LFP | MTI Online Store